Sevrene® 3582-70A
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Vi-Chem Corporation |
| Trademark: | Sevrene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PnNaNR_Sevrene-3582-70A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sevrene® 3582-70A is a Thermoplastic Elastomer (TPE) material. It is available in North America. Typical application of Sevrene® 3582-70A: Automotive |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.940 | g/cm³ | ASTM D792A, ISO 1183/A |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 69 | ASTM D2240, ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(100% Strain) | 2.20 | MPa | ISO 37 |
| Tensile Stress 2(Yield) | 11.2 | MPa | ISO 37 |
| Tensile Elongation 3(Break) | 940 | % | ISO 37 |
| Tear Strength 4 | 30 | kN/m | ISO 34-1 |
| Compression Set | ASTM D395, ISO 815 | ||
| 23°C, 168 hr | 25 | % | |
| 100°C, 168 hr | 58 | % |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (80°C, 1000 hr) | 2.0 | % | ASTM D412, ISO 188 |
| Change in Ultimate Elongation in Air (80°C, 1000 hr) | -19 | % | ASTM D412, ISO 188 |
| Thermal | Nominal Value | ||
|---|---|---|---|
| Cold Flexibility (-30°C) 5 | No cracks |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Fogging 6 | |||
| 38°C | 87 | % | |
| 95°C | 87 | % |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Arizona Weathering 7 | 0.100Pass (Black) | SAE J1976 | |
| Florida Weathering 8 | 1.14Pass (Black) | SAE J1976 | |
| Weather Resistance | SAE J1960 | ||
| -- 9 | 0.500Pass (Black) | ||
| -- 10 | Pass (Black) |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 46 | mm/min | FMVSS 302 |
| Note Message | |
|---|---|
| 1 . | 500 mm/min |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| 4 . | Method Ba, Angle (Unnicked), 500 mm/min |
| 5 . | FLTM BO-102-01 |
| 6 . | SAE J1756-94, 6 hrs |
| 7 . | 2 years, Delta E |
| 8 . | 2 Years, Delta E |
| 9 . | Interior Xenon, 1240.8 kj/m², Delta E |
| 10 . | Exterior Xenon Arc, 2500 kj/m², Delta E |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Borstar® LE8706 | Borealis AG | LLDPE | Borstar® |
| Kingfa FW-650 | Kingfa | ABS | Kingfa |
| MACOMASS PP MM-PP BG 84 | MACOMASS Verkaufs AG | PP Copolymer | MACOMASS PP |
| OTECH ALLOY OTO9060LSZH - Riser Insulation | OTECH Corporation | TP, Unspecified | OTECH ALLOY |
| LNP™ VERTON™ RV00AES compound | SABIC Innovative Plastics | Nylon 66 | LNP™ VERTON™ |