INTEGRAL™ 630 Polyolefin Adhesive Film is a heat-activated adhesive film specifically designed for bonding to steel and flexible polyolefins. New experimental films are continually being developed. Please discuss your particular application needs with your Dow representative. General Characteristics:
|
General Information | |
---|---|
Appearance |
|
Forms |
|
Films | Nominal Value | Unit | Test Method |
---|---|---|---|
Film Thickness - Tested | 18 | µm | ASTM D374 |
Film Thickness - Recommended / Available | 0.7-2.0 mil (18-51 µm) | ||
Secant Modulus | ASTM D882 | ||
1% Secant, MD : 18 µm | 384 | MPa | |
2% Secant, MD : 18 µm | 246 | MPa | |
1% Secant, TD : 18 µm | 422 | MPa | |
2% Secant, TD : 18 µm | 259 | MPa | |
Tensile Strength | ASTM D882 | ||
MD : Yield, 18 µm | 25.9 | MPa | |
TD : Yield, 18 µm | 16.1 | MPa | |
MD : Break, 18 µm | 20.8 | MPa | |
TD : Break, 18 µm | 15.5 | MPa | |
Tensile Elongation | ASTM D882 | ||
MD : Yield, 18 µm | 160 | % | |
TD : Yield, 18 µm | 460 | % | |
MD : Break, 18 µm | 160 | % | |
TD : Break, 18 µm | 460 | % | |
Elmendorf Tear Strength | ASTM D1922 | ||
MD : 18 µm | 200 | g | |
TD : 18 µm | 150 | g | |
Yield (25.4 µm) | 42.7 | m²/kg | Internal Method |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
SHIN-A SE-320P | SHIN-A T&C | Epoxy | SHIN-A |
UNIPA® lm | Nytef Plastics, Ltd. | Nylon 612 | UNIPA® |
Arak HDPE BL5 | Shazand (Arak) Petrochemical Corporation | HDPE | Arak HDPE |
Flontech® FT-BRR25-CF10-M5-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
Sylvin 8309-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |