BJB Polyurethane TC-885 FR REV 1
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Polyurethane |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PlCTTg_BJB-Polyurethane-TC-885-FR-REV-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TC-885 A/B FR REV 1 produces a high impact rigid 78 Shore D material that is commonly used to make computer housings, models of all kinds, artwork, and can also be used for electronic component enclosures. It provides a working time of 6 minutes. PRODUCT HIGHLIGHTS:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- 1 | 1.10 | g/cm³ | |
| -- | 1.26 | g/cm³ | |
| -- 2 | 1.38 | g/cm³ | |
| Specific Volume | 0.816 | cm³/g |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time | 7.0 | min | |
| Work Time 3(25°C) | 6.0 | min |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.070 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 76 to 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1540 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 41.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 20 | % | ASTM D638 |
| Flexural Modulus | 1830 | MPa | ASTM D790 |
| Flexural Strength | 66.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 30 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 87.8 | °C | |
| 1.8 MPa, Unannealed | 78.3 | °C | |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 75°C, 1.20 mm | Pass | ||
| 75°C, 1.30 mm | Pass |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Part B | Mix Ratio by Weight: 85, Mix Ratio by Volume: 68 | ||
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity | ASTM D2393 | ||
| 25°C 4 | 310 | cP | |
| 25°C 5 | 3200 | cP | |
| 25°C 6 | 75.0 | cP | |
| Demold Time (25°C) | 60 to 120 | min | |
| Post Cure Time (25°C) | 120 to 170 | hr |
| Note Message | |
|---|---|
| 1 . | Part A |
| 2 . | Part B |
| 3 . | 100g mass |
| 4 . | Mixed |
| 5 . | Part B |
| 6 . | Part A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™-C TFC84 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| UNIVAL™ DMDA-6230 NT 7 | The Dow Chemical Company | HDPE | UNIVAL™ |
| NaturePlast PLE 005 | NaturePlast | PLA | NaturePlast |
| ELIX™ 118HF | ELIX Polymers, S. L. | ABS | ELIX™ |
| LUVOCOM® 1105-8135/OR | Lehmann & Voss & Co. | PEEK | LUVOCOM® |