PRIMACOR™ 3150 is an ethylene acrylic acid copolymer designed for extrusion/coextrusion coating and laminating resin for flexible packaging applications. It provides excellent adhesion to metallic, paper and polyethylene substrates, and offers good draw- down, heat sealability and oil and grease resistance.
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.924 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) 1(190°C/2.16 kg) | 11 | g/10 min | ASTM D1238, ISO 1133 |
| Comonomer Content 2 | 3.0 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield, molding | 8.79 | MPa | ASTM D638, ISO 527-2 |
| Fracture, molding | 12.3 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, Compression Molded) | 590 | % | ASTM D638, ISO 527-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 88.9 | °C | ASTM D1525, ISO 306 |
| Melting Temperature (DSC) | 104 | °C | Internal method |
| Extrusion | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Temperature | 260 - 290 | °C | |
| Neck-in (288°C, 25.4 µm) | 63.5 | mm | Internal method |
| Minimum coating thickness | 10 | µm | Internal method |
| Minimum coating weight | 9.8 | g/m² | Internal method |
| Extrusion instructions |
|---|
| 挤出涂层薄膜的制造条件：用于处理此树脂的设备应由耐腐蚀材料制成。建议模具和适配器采用不锈钢和/或双面镀铬或镀镍。 螺杆尺寸：3.5 英寸 (89 mm)；30:1 L/D 模具间隙：20 密尔 (0.508 mm) 模具：30 英寸模具切边至 24 英寸 熔体温度：550°F (288°C) 输出：250 磅/小时 气隙：6 英寸 (152 mm) |
| Note Message | |
|---|---|
| 1 . | As measured during production. |
| 2 . | The comonomer content measured by Dow attribute method has the same accuracy as ASTM D 4094. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRE-ELEC® PA 1406 | Premix Oy | Nylon 6 | PRE-ELEC® |
| TITANZEX® HM5000 | Lotte Chemical Titan (M) Sdn. Bhd. | HDPE | TITANZEX® |
| Toyolac® 100-G10 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| ALCUDIA® HDPE 49070-UV | REPSOL | HDPE | ALCUDIA® HDPE |
| Geon™ Vinyl Wire & Cable WJKC306 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Wire & Cable |