Order Products : sales@su-jiao.com
AQUAFORCE® PA66 G60-01 SCHWARZ
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LEIS Polytechnik - polymere Werkstoffe GmbH |
| Trademark: | AQUAFORCE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PkVxXf_AQUAFORCE-PA66-G60-01-SCHWARZ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| polyamide 6.6 + 60% glass fibres, heat stabilized, potable water and food grade |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.69 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | 0.10 to 0.50 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 3.1 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.1 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| 23°C 2 | -- | 11000 | MPa | |
| 23°C 3 | -- | 14200 | MPa | |
| 23°C | 20500 | -- | MPa | |
| Tensile Stress | ISO 527-2 | |||
| 23°C 4 | -- | 130 | MPa | |
| 23°C 5 | -- | 165 | MPa | |
| 23°C | 240 | -- | MPa | |
| Tensile Strain | ||||
| Break, 23°C 6 | -- | 4.0 | % | ISO 527-2 |
| Break, 23°C | 2.6 | -- | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| 23°C 7 | -- | 26 | kJ/m² | |
| 23°C 8 | -- | 18 | kJ/m² | |
| 23°C | 14 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| 23°C 9 | -- | 70 | kJ/m² | |
| 23°C 10 | -- | 80 | kJ/m² | |
| 23°C | 85 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature (DSC) 11 | 260 | -- | °C | ISO 3146 |
| Note Message | |
|---|---|
| 1 . | 60mm x 60mm x 2mm |
| 2 . | Saturated in Water |
| 3 . | Testing according to ISO 527ISO 1110 |
| 4 . | Saturated in Water |
| 5 . | Testing according to ISO 527ISO 1110 |
| 6 . | Saturated in Water |
| 7 . | Saturated in Water |
| 8 . | Testing according to ISO 179/ISO 1110 |
| 9 . | Saturated in Water |
| 10 . | Testing according to ISO 179/ISO 1110 |
| 11 . | 10K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIME TPO E-2900 | Prime Polymer Co., Ltd. | PP Homopolymer | PRIME TPO |
| Sarlink® TPV X11059DB | Teknor Apex Company | TPV | Sarlink® TPV |
| ALTECH® PA6 C 2035/507 GF35 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| Comtrex Flexible PVC® 63XCF | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | Comtrex Flexible PVC® |
| ESENTTIA 02H82-AC | Polipropileno del Caribe S.A. | PP Homopolymer | ESENTTIA |