| Zenite 5244L is a 40% glass/mineral reinforced LCP resin with improved toughness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.71 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.40 | % | ISO 294-4 |
| Flow direction | 0.10 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 14000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 131 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.7 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 13100 | MPa | ISO 178 |
| Flexural Stress (23°C) | 198 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 17 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 27 | kJ/m² | ISO 179/1eU |
| Unnotched Izod Impact Strength (23°C) | 28 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 285 | °C | ISO 75-2/A |
| Melting Temperature 1 | 318 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 6.0E-6 | cm/cm/°C | ISO 11359-2 |
| Lateral | 4.8E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Relative Permittivity (2.05 GHz) | 4.18 | Internal method | |
| Dissipation Factor (2.05 GHz) | 4.0E-3 | Internal method |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 320 - 330 | °C | |
| Middle Temperature | 335 - 345 | °C | |
| Front Temperature | 335 - 345 | °C | |
| Nozzle Temperature | 335 - 345 | °C | |
| Processing (Melt) Temp | 325 - 345 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 50.0 - 150 | MPa | |
| Holding Pressure | 50.0 - 150 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Feed Temperature: 40 to 60°CZone 4 Temperature: 335 to 345°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA6 A1RG6301 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 6 | Shandong PA6 |
| TOYOBO Urethane E2090A | TOYOBO America, Inc. | PUR-Capro | TOYOBO Urethane |
| Ad-Tech Urethanes LUC-4190 | Ad-Tech Plastic Systems Corp. | TSU | Ad-Tech Urethanes |
| Baoding 67I80 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyester | Baoding |
| Braskem PP RP 347 | Braskem | PP Random Copolymer | Braskem PP |