Sipolprene® 35180 WB
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | SIPOL S.p.A |
| Trademark: | Sipolprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PizeG3_Sipolprene-35180-WB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sipolprene® 35180 WB is an ether ester thermoplastic elastomer (TPC-ET), developed and manufactured by Sipol, with a nominal hardness of Shore D 35, a low modulus, and a rheological behaviour, which makes it suitable for injection molding and extrusion processing. Sipolprene® 35180 WB comes in a dry blend UV-stabilised and black color version. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183, ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 34 | g/10 min | ASTM D1238, ISO 1133 |
| Water Absorption 1(23°C, 24 hr) | 0.73 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 35 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 26.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 800 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 45.0 | MPa | ASTM D790, ISO 178 |
| Abrasion Resistance | 26.0 | mm³ | DIN 53516 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 113 | kN/m | ASTM D1004 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 111 | °C | ISO 306/A50, ASTM D1525 2 |
| Peak Melting Temperature | 177 | °C | ASTM D3418, ISO 3146 |
| Note Message | |
|---|---|
| 1 . | Immersion |
| 2 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zeoforte® ZSC3195CX | Zeon Corporation | NBR | Zeoforte® |
| NatureFlex™ NE30 (19µ) | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| Karina CLEAR PVC COMPOUND 80/208-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina BLACK PVC COMPOUND 650-48/1-GARAP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PERCOM® KHS09 | A. Schulman Europe | PP Homopolymer | PERCOM® |