LNP™ THERMOCOMP™ JF006LXZ compound
| Category: | PESU , Polyethersulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PiuaOp_LNPTHERMOCOMPJF006LXZcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP JF006LXZ is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Low Extractible. Also known as: LNP* THERMOCOMP* Compound JF-1006 LE Product reorder name: JF006LXZ |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.61 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.20 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.70 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.69 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.25 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.30 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 9790 | MPa | ASTM D638 |
| -- | 10200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 113 | MPa | ASTM D638 |
| Fracture | 99.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 1.8 | % | ASTM D638 |
| Fracture | 1.4 | % | ISO 527-2 |
| Flexural Modulus | 9240 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | |||
| -- | 172 | MPa | ASTM D790 |
| -- | 222 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 2 | 6.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 430 | J/m | ASTM D4812 |
| 23°C 3 | 30 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 13.0 | J | ASTM D3763 |
| -- | 3.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 218 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 212 | °C | ASTM D648 |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 3.1E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 3.6E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-4001 | Teknor Apex Company | TPE | Telcar® |
| Chemlon® 182 | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Ducor® 3300L | Ducor Petrochemicals BV | PP Impact Copolymer | Ducor® |
| LUVOCOM® 1105-8356 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| Petlon R-Prime A2-00-00-BK | Petlon Polymers Ltd | Nylon 6 | Petlon R-Prime |