| Category: | PPA , Polyphthalamide |
| Manufacturer: | Ensinger GmbH |
| Trademark: | TECACOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PiFKUq_TECACOMPPPALDSblack4108.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Main features
Target Industries
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.96 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 16 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/5.0 kg) | 8.40 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 1.1 | % | ISO 294-4 |
| Flow | 1.0 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | < 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8750 | MPa | ISO 527-2/50 |
| Tensile Stress | 95.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 1.7 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 30 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 203 | °C | ISO 75-2/A |
| Glass Transition Temperature | 100 - 140 | °C | DIN 53765 |
| Melting Temperature | 285 - 315 | °C | DIN 53765 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 50 to 100°C | 3.8E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 100 to 150°C | 5.3E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 150 to 200°C | 8.5E-5 | cm/cm/°C | ISO 11359-2 |
| Horizontal : 50 to 100°C | 4.9E-5 | cm/cm/°C | ISO 11359-2 |
| Horizontal : 100 to 150°C | 7.2E-5 | cm/cm/°C | ISO 11359-2 |
| Horizontal : 150 to 200°C | 9.3E-5 | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 860 | J/kg/°C | DIN EN 821 |
| Thermal Conductivity | DIN EN 821 | ||
| -- 1 | 0.80 | W/m/K | DIN EN 821 |
| -- 2 | 1.0 | W/m/K | DIN EN 821 |
| Service Temperature | |||
| long term | 150 | °C | |
| short term | 250 | °C | |
| Thermal Diffusivity | DIN EN 821 | ||
| In-plane | 0.560 | cSt | DIN EN 821 |
| Through-plane | 0.440 | cSt | DIN EN 821 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Adhesion Strength - metal path | 28.2 | MPa | |
| Lazer Marking | |||
| Forward moving | 2.0 - 3.0 | m/sec | |
| Frequency | 100 - 200 | kHz | |
| Power | 2.00 - 6.00 | Watts |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.0E+12 | ohms | DIN EN 61340 |
| Volume Resistivity | 4.7E+13 | ohms·cm | DIN EN 61340 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | HB | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 320 - 340 | °C | |
| Mold Temperature | 150 - 170 | °C |
| Note Message | |
|---|---|
| 1 . | Through-plane |
| 2 . | In-plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PTS PBT-30GFR-BK | Polymer Technology and Services, LLC | PBT | PTS |
| Shandong PA610 GYELVN | Shandong Guangyin New Materials Co., Ltd. | Nylon 610 | Shandong PA610 |
| Sinvicomp SRF3803 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| NILSAN S GP | Taro Plast S.p.A. | ABS | NILSAN |
| Nylene® 132-250 | Custom Resins Group | Nylon 66 | Nylene® |