Badamid® A70 GK15 TM-Z3
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Pgulg6_Badamid-A70-GK15-TM-Z3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Badamid®A70 GK15 TM-Z3 is a polyamide 66 (nylon 66) material containing 15% glass beads. This product is available in Europe,. Badamid®The main characteristics of A70 GK15 TM-Z3 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.22 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 6.2 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3700 | 1900 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 83.0 | 55.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 17 | 45 | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 12 | 16 | kJ/m² | ISO 179/1eA |
| 23°C | 16 | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact (23°C) | 17 | 24 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 1 | ||||
| 0.45 MPa, not annealed | 225 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 110 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 262 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.40 | 5.40 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.015 | 0.16 | IEC 60250 | |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | UL 94 | |
| 1.60 mm | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 Short-Term Heat Resistance, IEC 216, 20000 hrs: 160°CLong-Term Heat Resistance, IEC 216, 50% decrease of yield stress: 95°C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 110x10x4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAMID™ H24M10 | Mando Advanced Materials Co., Ltd. | ABS+Nylon | TEKAMID™ |
| NuSil MED-4159 | NuSil Technology | Silicone | NuSil |
| Bergamid™ B700 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| Indorama PET 1101 B-PET | Indorama Ventures Polymers México | PET | Indorama PET |
| ULTEM™ HU1010 resin | SABIC Innovative Plastics | PEI | ULTEM™ |