DIAMALOY ABSPC 7801
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | DIAMALOY ABSPC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PgFUru_DIAMALOY-ABSPC-7801.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DIAMALOY ABSPC 7801 is a Polycarbonate + ABS (PC+ABS) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1(265°C/5.0 kg) | 29 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 2 | 2320 | MPa | ASTM D638 |
| Tensile Strength 3(Yield) | 40.9 | MPa | ASTM D638 |
| Flexural Modulus - Tangent 4(3.18 mm) | 2020 | MPa | ASTM D790 |
| Flexural Strength 5(5.0% Strain, 3.18 mm) | 66.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 550 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.18 mm | 106 | °C | |
| 1.8 MPa, Unannealed, 6.35 mm | 110 | °C | |
| Vicat Softening Temperature | 137 | °C | ASTM D1525 6 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 70 | % | |
| Suggested Max Regrind | 30 | % | |
| Rear Temperature | 230 to 260 | °C | |
| Middle Temperature | 235 to 265 | °C | |
| Front Temperature | 238 to 272 | °C | |
| Nozzle Temperature | 238 to 272 | °C | |
| Processing (Melt) Temp | 238 to 272 | °C | |
| Mold Temperature | 40.0 to 100 | °C | |
| Back Pressure | 0.345 to 1.03 | MPa |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® D6975CT | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| S&E PVC GA-1060 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E PVC |
| TECHNAMID® A A-SV30-TAP | Poly Plastic | Nylon 66 | TECHNAMID® A |
| TOTAL Polypropylene PPH 6080 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Styropek® BF 395S | Styropek S.A. de C.V. | PS (EPS) | Styropek® |