Category: | Nylon 6 , Polyamide 6 |
Manufacturer: | Vamp Tech |
Trademark: | DENYL |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | PgEPL3_DENYL-6-3016.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
PA 6, 30% glass microspheres and fiber filled, not Flame Retardant compound, good mechanical properties. |
General Information | |
---|---|
Filler / Reinforcement |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
Molding Shrinkage | ASTM D955 | ||
Flow | 0.80 | % | |
Across Flow | 1.0 | % | |
Water Absorption (Saturation) | 1.6 | % | ASTM D570 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Modulus | 6000 | MPa | ASTM D638 |
Tensile Strength (Yield) | 100 | MPa | ASTM D638 |
Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact Strength | 7.0 | kJ/m² | ISO 180/A |
Unnotched Izod Impact Strength | 40 | kJ/m² | ISO 180 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Deflection Temperature Under Load (1.8 MPa, Unannealed) | 200 | °C | ASTM D648A |
Vicat Softening Temperature | 205 | °C | ASTM D1525 1 |
RTI Elec | 120 | °C | UL 746 |
RTI Imp | 120 | °C | UL 746 |
RTI Str | 120 | °C | UL 746 |
Injection | Nominal Value | Unit | |
---|---|---|---|
Drying Temperature | 90.0 | °C | |
Drying Time | 3.0 | hr | |
Processing (Melt) Temp | 260 | °C | |
Mold Temperature | 100 | °C |
Note Message | |
---|---|
1 . | Loading 2 (50 N) |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
Makrolon® EM9417 | Covestro - Polycarbonates | PC | Makrolon® |
Sinvicomp SIC3704BUV | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
Badamid® C70 FR HF | Bada AG | Nylon 66/6 | Badamid® |
APEX® 90-A472R-90-NT | Teknor Apex Company | PVC, Flexible | APEX® |
Durez® 33183 | SBHPP | Phenolic | Durez® |