LubriOne™ NN-30CF/15T-02S black
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | LubriOne™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Pf3yK8_LubriOne-NN-30CF-15T-02S-black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 3.6 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.10 to 0.20 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 19100 | MPa | ISO 527 |
| Tensile Strength 2(Break) | 162 | MPa | ISO 527 |
| Tensile Elongation 3(Break) | 1.0 to 2.0 | % | ISO 527 |
| Flexural Modulus | 13600 | MPa | ISO 178 |
| Flexural Strength | 210 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 21 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 260 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 240 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 288 to 299 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® C49C10 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| RheTech Thermoplastic Polyolefin FT5250-650UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Arnite® T06 200 (extrusion) | DSM Engineering Plastics | PBT | Arnite® |
| Favorite EVA300 | Favorite Plastics | EVA | Favorite |
| LEXAN鈩?EXL1810T resin | SABIC Innovative Plastics | PC | LEXAN™ |