LNP™ THERMOCOMP™ UFW49S compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PeQSWK_LNP-THERMOCOMP-UFW49S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP UFW49S is a compound based on Polyphthalamide resin containing 45% Glass Fiber, 20% Wollastonite. Added features of this material include: Heat Stabilized, Low Warpage. Also known as: LNP* THERMOCOMP* Compound UFM-3249 HS Product reorder name: UFW49S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.85 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 192 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.1 | % | ISO 527-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 1.7E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 2.7E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 310 to 321 | °C | |
| Middle Temperature | 316 to 327 | °C | |
| Front Temperature | 327 to 338 | °C | |
| Processing (Melt) Temp | 316 to 332 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® F7895 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| TORZEN® G3000HR BK34 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| Nypol® PA A3 T30 UV PRTA010 NR444 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Formolene® 4142T | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |
| Laprene® 830000859 | SO.F.TER. SPA | SEBS | Laprene® |