RTP 6042-40A MD
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PdysTE_RTP-6042-40A-MD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ISO 10993 Tested |
| General Information | |
|---|---|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Moisture Content | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 40 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(100% Strain, 3.18 mm) | 1.17 | MPa | ASTM D412 |
| Tensile Strength 2(Yield, 3.20 mm) | 5.86 | MPa | ASTM D412 |
| Tensile Elongation 3(Break) | 500 | % | ASTM D412 |
| Tear Strength 4 | 22.8 | kN/m | ASTM D624 |
| Compression Set 5 | ASTM D395B | ||
| 23°C, 22 hr | 20 | % | ASTM D395B |
| 70°C, 22 hr | 75 | % | ASTM D395B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Dew Point | < -17.8 | °C | |
| Processing (Melt) Temp | 193 - 238 | °C | |
| Mold Temperature | 21.1 - 48.9 | °C |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Note Message | |
|---|---|
| 1 . | Mouth die C, 510mm/min |
| 2 . | C mold, 500 mm/min |
| 3 . | Mouth die C, 500 mm/min |
| 4 . | C mould |
| 5 . | Type 2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 TFE 5 SI 2 | RTP Company | Acetal (POM) Copolymer | RTP |
| SABIC® HDPE FI1157 | Saudi Basic Industries Corporation (SABIC) | HDPE, HMW | SABIC® HDPE |
| Vyncolit® BXE7665 | Vyncolit N.V. | Phenolic | Vyncolit® |
| EVERLON® TC-55C | Ever Polymer Co., Ltd. | SEBS | EVERLON® |
| MAJORIS EW460 | AD majoris | PP Copolymer | MAJORIS |