Fasal® BIO 322
| Category: | Biodeg Polymers , Biodegradable Polymers |
| Manufacturer: | Fasal Wood KG |
| Trademark: | Fasal® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PcThFK_Fasal-BIO-322.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Fasal BIO 322 is a wood based material for injection moulding applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.28 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4930 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 51.5 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.3 | % | ISO 527-2 |
| Flexural Modulus | 4640 | MPa | ISO 178 |
| Flexural Stress | 78.9 | MPa | ISO 178 |
| Flexural Strain | 1.2 | % | ISO 178 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Renewable Content | 100 | % | |
| Biobased Content | 100 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 8.7 | kJ/m² | ISO 179/1fU |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 170 | °C | |
| Middle Temperature | 180 | °C | |
| Front Temperature | 180 | °C | |
| Nozzle Temperature | 190 | °C | |
| Mold Temperature | 10.0 - 30.0 | °C |
| Injection instructions |
|---|
| Screw speed: 60 - 70% of maximumDynamic pressure: 40% of maximumInjection pressure: approx. 20 % higher than with plastics |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren I180E (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| Flontech® FT-CAF20-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Hostacom 75F4-4 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Karina WHITE PVC COMP. -E 800D10/ 7-A-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| neogol® 35 C UG | API SpA | TPO (POE) | neogol® |