CELEX™ 5200HF
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CELEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PbIA7U_CELEX-5200HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CELEX 5200HF is a non-halogen ignition resistant PC/ABS alloy. It combines the superior physical properties of PC and the excellent processability of ABS. CELEX 5200HF is designed with excellent flow for use in monitor housing and instrument panel. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 19 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.20 mm, Injection Molded) | 2450 | MPa | ASTM D638 |
| Tensile Strength (Yield, 3.20 mm, Injection Molded) | 55.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.20 mm, Injection Molded) | 100 | % | ASTM D638 |
| Flexural Modulus (3.20 mm, Injection Molded) | 2600 | MPa | ASTM D790 |
| Flexural Strength (3.20 mm, Injection Molded) | 88.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 3.20 mm, Injection Molded | 220 | J/m | |
| 23°C, 3.20 mm, Injection Molded | 750 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm, Injection Molded) | 83.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 100 | °C | ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 2(1.60 mm) | V-0 5VB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 190 to 220 | °C | |
| Middle Temperature | 200 to 225 | °C | |
| Front Temperature | 205 to 235 | °C | |
| Nozzle Temperature | 210 to 235 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h) |
| 2 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMIKASUPER® LCP E6308AS | Sumitomo Chemical Co., Ltd. | LCP | SUMIKASUPER® LCP |
| Ultramid® 1503-2 BK ND3007 | BASF Corporation | Nylon 66 | Ultramid® |
| Elastron® G G501.A50.N.PS | Elastron USA, Inc. | SEBS | Elastron® G |
| HiFill® PA6/6 GF13 L YAG | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Hostacom ERC 213N NAT | LyondellBasell Industries | PP Copolymer | Hostacom |