UNITIKA Nylon 6 A1030JR
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | UNITIKA Plastics Division |
| Trademark: | UNITIKA Nylon 6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PafoTR_UNITIKA-Nylon-6-A1030JR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
UNITIKA Nylon 6 A1030JR is a Polyamide 6 (Nylon 6) material. It is available in Asia Pacific or North America. Important attributes of UNITIKA Nylon 6 A1030JR are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | 1.14 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 3.20 mm | 1.1 | 1.1 | % | |
| Flow : 3.20 mm | 0.90 | 0.90 | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 1.8 | 1.8 | % | |
| Equilibrium, 23°C, 50% RH | 2.8 | 2.8 | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | 85 | ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2900 | 1200 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 82.0 | 55.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | |||
| Yield | 4.0 | 22 | % | |
| Break | 30 | 150 | % | |
| Flexural Modulus | 2800 | 1200 | MPa | ISO 178 |
| Flexural Stress | 105 | 49.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 4.0 | 31 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | No Break | No Break | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 170 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 61.0 | -- | °C | ISO 75-2/A |
| CLTE - Flow | 9.6E-5 | 9.6E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 3.0E+15 | 8.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm) | 37 | 33 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.40 | 3.70 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | 0.080 | IEC 60250 | |
| Comparative Tracking Index | 600 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.840 mm) | V-2 | V-2 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren M800E (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Random Copolymer | Sanren |
| Braskem PP H 504 XP | Braskem | PP Homopolymer | Braskem PP |
| DINALON® PA 6 IGNÍFUGA 30% FV | Grupo Repol | Nylon 6 | DINALON® |
| Felix Compounds Calcium Carbonate | Felix Compounds | PP, Unspecified | Felix Compounds |
| LUVOCOM® 20-7094 | Lehmann & Voss & Co. | PPA | LUVOCOM® |