KPOL-PP K-PPC 1.50

Category:	PP Impact Copolymer , Polypropylene Impact Copolymer
Manufacturer:	KPOL Chem Co.
Trademark:	KPOL-PP
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	PaXrQv_KPOL-PP-K-PPC-1-50.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Polypropylene Heterophasic Copolymer

Characteristics

The KPOL® resin is a propylene impact copolymer designed for injection molding applications, Excellent Balance of Stiffness and Impact Strength at low temperatures, Contains Nucleating , Good Mold Release.

Superior Drop Impact at Refrigeration Temperature, Very High Flexural Modulus. Also is suitable for technical components: toys, sports, equipment, leisure goods, automotive, pallets, crates and pails.

Applications

Injection / Automobile applications, Battery case, Home appliances, Industrial parts for electronic. Thermoformed packages with high impact strength; Blown packages and technical parts in general; sheet extrusion.

General Information
Additive	Antioxidant Nucleating Agent
Features	Antioxidant Good Impact Resistance Good Mold Release Good Stiffness Impact Copolymer Low Temperature Resistant Nucleated
Uses	Appliances Automotive Applications Battery Cases Crates Electrical/Electronic Applications Industrial Parts Packaging Pallets Thermoforming Applications Toys
Agency Ratings	FDA 21 CFR 177.1520
Processing Method	Blow Molding Extrusion Injection Molding Sheet Extrusion

Physical	Nominal Value	Unit	Test Method
Density	0.900	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	1.5	g/10 min	ASTM D1238

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	78		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Yield)	25.0	MPa	ASTM D638
Tensile Elongation ²(Break)	10	%	ASTM D638
Flexural Modulus - 1% Secant	1200	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (-20°C)	50	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	88.0	°C	ASTM D648
Vicat Softening Temperature	150	°C	ASTM D1525 ³

Note Message
1 .	Type IV, 50 mm/min
2 .	Type IV, 50 mm/min
3 .	Rate A (50°C/h), Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
Quadraflex™ ALE-85A-B30	Biomerics, LLC	TPU-Polyether	Quadraflex™
TPV Elastoprene® N55A-i	ELASTORSA Elastomeros Riojanos S.A.	PP+EPDM	TPV Elastoprene®
Alkatuff® LL0228	Qenos Pty Ltd	LLDPE	Alkatuff®
Anjacom® 055/80-GF20 Black 91210	Almaak International GmbH	PC+ABS	Anjacom®
Hostacom TRC 333N G72825	LyondellBasell Industries	PP Copolymer	Hostacom