CABELEC® CA4918
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Cabot Corporation |
| Trademark: | CABELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PaA4ar_CABELEC-CA4918.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CABELEC® 4918 is an electrically conductive compound based on conductive carbon black and a modified low density polyethylene resin. Its electrical and mechanical properties are permanent and are not dependent on atmospheric conditions. CABELEC® 4918 has been specially designed for packaging and product handling applications where freedom from the hazard of electrostatic discharge is necessary. Examples of use are in handling of explosive powders, pigments and electronic components. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.06 | g/cm³ | Internal Method |
| Melt Mass-Flow Rate (MFR) 2 | ISO 1133 | ||
| 190°C/10.0 kg | 3.5 | g/10 min | |
| 190°C/5.0 kg | 0.80 | g/10 min |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 3 | ISO 527-3/500 | ||
| MD : Yield, 100 µm | 11.5 | MPa | |
| TD : Yield, 100 µm | 11.0 | MPa | |
| MD : Break, 100 µm | 20.5 | MPa | |
| TD : Break, 100 µm | 19.8 | MPa | |
| Tensile Elongation 4 | ISO 527-3/500 | ||
| MD : Yield, 100 µm | 23 | % | |
| TD : Yield, 100 µm | 22 | % | |
| MD : Break, 100 µm | 580 | % | |
| TD : Break, 100 µm | 430 | % | |
| Trouser Tear 5 | ASTM D1938 | ||
| MD : 50.0 µm | 46.0 | kN/m | |
| TD : 50.0 µm | 31.0 | kN/m | |
| Elmendorf Tear Strength 6 | ASTM D1922 | ||
| MD : 100.0 µm | 210.0 | kN/m | |
| TD : 100.0 µm | 200.0 | kN/m |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 7(0.100 mm) | 5.1E+3 | ohms | Internal Method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Cylinder Zone 1 Temp. | 180 to 200 | °C | |
| Cylinder Zone 2 Temp. | 180 to 200 | °C | |
| Cylinder Zone 3 Temp. | 180 to 200 | °C | |
| Cylinder Zone 4 Temp. | 180 to 200 | °C | |
| Cylinder Zone 5 Temp. | 180 to 200 | °C | |
| Melt Temperature | < 230 | °C | |
| Die Temperature | 200 | °C |
| Note Message | |
|---|---|
| 1 . | CTM E023 |
| 2 . | CTM E005 |
| 3 . | CTM E041 |
| 4 . | CTM E041 |
| 5 . | CTM E048, 250 mm/min |
| 6 . | CTM E048B |
| 7 . | CTM E042B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polyvel PLA PE-L01 PLA Matte Finish | Polyvel Inc. | PLA | Polyvel PLA |
| Sangel® WLE100 | Unigel Plásticos | SAN | Sangel® |
| Blendfor® A 4000/V0 NERO | SO.F.TER. SPA | PC+ABS | Blendfor® |
| APEX® 90-P513A-85-NT | Teknor Apex Company | PVC+PUR | APEX® |
| Ducor® 1104K | Ducor Petrochemicals BV | PP Homopolymer | Ducor® |