SAXALEN™ PPH319FX21
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | SAX Polymers |
| Trademark: | SAXALEN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Pa6hRV_SAXALEN-PPH319FX21.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SAXALEN PPH319FX21 is an unfilled Polypropylene - Homopolymer intended for injection moulding. The product has flame retardant properties and suitable to produce thin-walled parts. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 28.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2100 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 36.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 6.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1200 | MPa | ISO 178 |
| Flexural Stress 2 | 35.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 2.0 | kJ/m² | |
| 23°C | 4.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 15 | kJ/m² | |
| 23°C | 85 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 2.0 | kJ/m² | |
| 23°C | 4.0 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 13 | kJ/m² | |
| 23°C | 55 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 60.0 mm Span) | 120 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 210 to 240 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECOLITE KM-450(J) | KYOCERA Chemical Corporation | Phenolic | TECOLITE |
| Sylvin 6034-85 Grey 9561 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ALTECH® PA66 A 1000/310 IM | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| Epoxies, Ect. 20-1710 | Epoxies, Etc. | Silicone Gel | Epoxies, Ect. |
| POCAN® S 1517 000000 | LANXESS GmbH | PBT | POCAN® |