SABIC® LLDPE PCG61
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PZtnd1_SABIC-LLDPE-PCG61.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LLDPE PCG61 is a hexene-linear low density polyethylene typically used for healthcare applications. Films made from this resin exhibit good mechanical, optical and hottack properties. Application Typical application for SABIC® LLDPE PCG61 are pharmaceutical films, bags and pouches requiring good impact strength, tear resistance, optical performance and hottack properties. Compliance to Regulations SABIC® LLDPE PCG6118NE complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 50 µm, blown film | 190 | MPa | ISO 527-3 |
| TD : 50 µm, blown film | 230 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 50 µm, blown film | 11.0 | MPa | ISO 527-3 |
| TD : Yield, 50 µm, blown film | 12.5 | MPa | ISO 527-3 |
| MD : Broken, 50 µm, blown film | 47.0 | MPa | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 40.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 630 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 800 | % | ISO 527-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength - Blown Film (50.0 µm) | 350 | J/cm | ASTM D4272 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Puncture Resistance - Blown Film (50.0 µm) | 750 | J/m | Internal method |
| Tear Strength 1 | ISO 6383-2 | ||
| MD : 50.0 µm | 100.0 | kN/m | ISO 6383-2 |
| TD : 50.0 µm | 400.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 106 | °C | ISO 306/A |
| Melting Temperature (DSC) | 124 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, Blown Film) | 57 | ASTM D2457 | |
| Haze (Blown Film) | 13 | % | ASTM D1003A |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film of 50 µm and BUR = 2 has been produced on Kiefel IBC with 140 kg/h. Die size 200 mm, die gap 2.7 mm. |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ F-300SP | Prime Polymer Co., Ltd. | PP Homopolymer | Prime Polypro™ |
| Sicostirolo CR H 3444 | Ravago Group | PS (HIPS) | Sicostirolo |
| Vyncolit® E 8354-19189-2 | Vyncolit N.V. | Epoxy | Vyncolit® |
| Fainplast PVC PH 76/A | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| KOPELEN J-320C | Lotte Chemical Corporation | PP Impact Copolymer | KOPELEN |