LNP™ STAT-KON™ JX89626 compound
| Category: | PESU , Polyethersulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PZRLBd_LNP-STAT-KON-JX89626-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON JX89626 is a compound based on Polyethersulfone containing Proprietary Fillers. Added feature of this material is: Electrically Conductive. Also known as: LNP* STAT-KON* Compound PDX-J-89626 Product reorder name: JX89626 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.10 to 0.30 | % | |
| Across Flow : 24 hr | 0.50 to 0.80 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.49 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.71 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11900 | MPa | ASTM D638 |
| -- | 11200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 163 | MPa | ASTM D638 |
| Break | 161 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.1 | % | ASTM D638 |
| Break | 2.2 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 10100 | MPa | ASTM D790 |
| -- 5 | 9680 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 226 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 238 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 49 | J/m | ASTM D256 |
| 23°C 7 | 6.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 600 | J/m | ASTM D4812 |
| 23°C 8 | 37 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 7.30 | J | ASTM D3763 |
| -- | 3.80 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 220 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 219 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 214 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 214 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 4.7E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 3.8E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0 to 5.0 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 343 to 354 | °C | |
| Middle Temperature | 360 to 371 | °C | |
| Front Temperature | 371 to 382 | °C | |
| Processing (Melt) Temp | 354 to 371 | °C | |
| Mold Temperature | 138 to 149 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SGH4500 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Chiao Fu PP PP212G20 NAT | Chiao Fu Enterprises Co., Ltd. | PP, Unspecified | Chiao Fu PP |
| Durolon® G2510 | Unigel Plásticos | PC | Durolon® |
| LUVOCOM® 3/CF/30 VP | Lehmann & Voss & Co. | Nylon 6 | LUVOCOM® |
| Nylux 66-GF33NAT | KMI Group, Inc. | Nylon 66 | Nylux |