LNP™ STAT-KON™ AX01706 compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PYzgH6_LNP-STAT-KON-AX01706-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON AX01706 is a compound based on ABS containing proprietary fillers. Added feature of this grade is: Electrically Conductive. Also known as: LNP* STAT-KON* Compound PDX-A-01706 Product reorder name: AX01706 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.50 to 0.70 | % | |
| Across Flow : 24 hr | 0.60 to 0.80 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.19 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.27 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2050 | MPa | ASTM D638 |
| -- | 2030 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 30.0 | MPa | ASTM D638 |
| Yield | 28.0 | MPa | ISO 527-2/5 |
| Break 3 | 27.0 | MPa | ASTM D638 |
| Break | 24.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 1.9 | % | ASTM D638 |
| Yield | 1.8 | % | ISO 527-2/5 |
| Break 5 | 5.8 | % | ASTM D638 |
| Break | 7.4 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2070 | MPa | ASTM D790 |
| -- 7 | 2030 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 52.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 52.0 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 46.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 42 | J/m | ASTM D256 |
| 23°C 10 | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 470 | J/m | ASTM D4812 |
| 23°C 11 | 25 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 13.4 | J | ASTM D3763 |
| -- | 3.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 96.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 97.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 88.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 85.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 8.5E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 8.8E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0 to 6.0 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Rear Temperature | 204 to 216 | °C | |
| Middle Temperature | 232 to 243 | °C | |
| Front Temperature | 266 to 277 | °C | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 71.1 to 82.2 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP5312 B1 | Spartech Polycom | PP, Unspecified | Spartech |
| ACCUTECH™ CP0436C20L1 | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| HiFill® PA11 GF30 L UV | Techmer Engineered Solutions | Nylon 11 | HiFill® |
| TechnoFin PP GF 30 | TechnoCompound GmbH | PP, Unspecified | TechnoFin |
| LUVOCOM® 70-9045 | LEHVOSS Group | PK | LUVOCOM® |