InnoTooling™ IE-644-02
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoTooling™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PYE7YR_InnoTooling-IE-644-02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| IE-644-02 is a tough, abrasion resistant elastomer formulated for room temperature hand-batch processing. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or TDI. IE-644-02 is ideal for very large parts as well as mass casting and tooling. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Hardener | 1.09 | g/cm³ | |
| Cured | 1.10 | g/cm³ | |
| Base Resin | 1.13 | g/cm³ | |
| Molding Shrinkage - Flow | 0.40 | % | ASTM D2566 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 320 | J/m | ASTM D256 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 26 Mix Ratio by Weight: 25 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 240 to 480 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.10 | Pa·s | |
| 25°C 2 | 3.0 | Pa·s | |
| 25°C 3 | 3.7 | Pa·s | |
| Curing Time 4 | 40 | hr | |
| Gel Time | 20 to 30 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 75 to 85 | ASTM D2240 | |
| Tensile Strength | 6.89 | MPa | ASTM D638 |
| Tensile Elongation at Break | 190 | % | ASTM D638 |
| Tear Strength | 26.3 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Mixed |
| 3 . | Resin |
| 4 . | 24 hours at 77°F + 16 hours at 150°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200.5 TFE 5 FR | RTP Company | Nylon 66 | RTP |
| SCHULAMID® 66 MV 5 FR | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| Sylvin 9963-75 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| FERREX® GPP30CN33HB-NA | Ferro Corporation | PP, Unspecified | FERREX® |
| Hangzhou Plastic PVC/PE/PVDC Laminated Film | Hangzhou Plastic Industry Co., Ltd. | Film, PVC/PE/PVDC | Hangzhou Plastic |