LNP™ LUBRICOMP™ ML004S compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PY2Qng_LNP-LUBRICOMP-ML004S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP ML004S is a compound based on Polypropylene resin containing 20% PTFE. Added features of this material include: Wear Resistant, Heat Stabilized. Also known as: LNP* LUBRICOMP* Compound ML-4040 HS Product reorder name: ML004S |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 2.0 to 4.0 | % | |
| Across Flow : 24 hr | 2.0 to 4.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.020 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2030 | MPa | ASTM D638 |
| -- | 1670 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 33.0 | MPa | ASTM D638 |
| Yield | 31.0 | MPa | ISO 527-2/5 |
| Break 3 | 30.0 | MPa | ASTM D638 |
| Break | 29.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 5.6 | % | ASTM D638 |
| Yield | 5.0 | % | ISO 527-2/5 |
| Break 5 | 15 | % | ASTM D638 |
| Break | 13 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 1760 | MPa | ASTM D790 |
| -- 7 | 1700 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 44.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 47.0 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.76 | ||
| vs. Itself - Static | 0.62 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 6.00 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 172 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 44 | J/m | ASTM D256 |
| 23°C 9 | 3.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 350 | J/m | ASTM D4812 |
| 23°C 10 | 22 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 6.02 | J | ASTM D3763 |
| -- | 1.38 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 119 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 105 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 65.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 60.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 9.1E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 4.0E-3 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 238 to 249 | °C | |
| Processing (Melt) Temp | 227 to 249 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Wire & Cable GA-509ORLT All Colors | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Wire & Cable |
| Sylvin 2943-90 Blue 8406 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TAROMID B 280 Z2 G6 | Taro Plast S.p.A. | Nylon 6 | TAROMID B |
| TOTAL Polypropylene PPC 9712 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| TECHNYL® AR 218 V50 BLACK | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |