PENTAMID A GV30 H1 RC black
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTAMID A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PWXEUY_PENTAMIDAGV30H1RCblack.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Normal viscosity, high heat stabilised polyamide 66, 30% glass fiber reinforced , ReCompound |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Recycled Content |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.36 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 0.80 | -- | % | ISO 294-4 |
| Flow | 0.50 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 5.0 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.5 | -- | % | ISO 62 |
| Viscosity Number | 130 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8200 | 6700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 140 | 115 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.5 | 5.0 | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 60 | 70 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 245 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 235 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Dielectric Strength | 35 | -- | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.50 | -- | IEC 60250 | |
| Comparative Tracking Index | 400 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.6 mm | HB | -- | UL 94 | |
| 3.2 mm | HB | -- | UL 94 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA66, MHRC, 14-080, GF30 | -- | ISO 1874 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.050 - 0.13 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 270 - 290 | °C | |
| Middle Temperature | 275 - 300 | °C | |
| Front Temperature | 280 - 290 | °C | |
| Processing (Melt) Temp | 270 - 300 | °C | |
| Mold Temperature | 60 - 100 | °C | |
| Injection Pressure | 78.0 | MPa | |
| Screw L/D Ratio | 18.0:1.0 to 22.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| YUNGSOX® PP 5350T | Formosa Polypropylene | PP Random Copolymer | YUNGSOX® PP |
| Vandar® 2122 | Celanese Corporation | PBT | Vandar® |
| Devlon 6GF30 | Devol® Engineering Polymers | TP, Unspecified | Devlon |
| Flexathene® PD907 | LyondellBasell Industries | Polyolefin, Unspecified | Flexathene® |
| Sylvin 2990-70 Clear 8382 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |