SAXAMID™ 226F6T3
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SAX Polymers |
| Trademark: | SAXAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PW0KSm_SAXAMID-226F6T3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SAXAMID 226F6T3 is a general purpose polyamide 6.6 injection-molding-grade reinforced with 30 % glass fibres. This compound shows its high mechanical strength over a long period and is able to perform at higher temperatures in combination with low frictioncoefficients and very good wear resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183 |
| Viscosity Number (H2SO4 (Sulphuric Acid)) | 150 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 175 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 8200 | MPa | ISO 178 |
| Flexural Stress 2 | 280 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 10 | kJ/m² | |
| 23°C | 12 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 70 | kJ/m² | |
| 23°C | 83 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 9.0 | kJ/m² | |
| 23°C | 12 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 67 | kJ/m² | |
| 23°C | 80 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 60.0 mm Span) | 240 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 250 | °C | ISO 306/B120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarnoform® 300 GF5 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| NEFTEKHIM PE 5122N | Nizhnekamskneftekhim Inc. | LLDPE | NEFTEKHIM PE |
| NYCOA Polyamide 2326 HS | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA Polyamide |
| AIE PC 1010F-T6 | Asia International Enterprise (Hong Kong) Limited | PC | AIE PC |
| Hifax EYG 382P C12716 | LyondellBasell Industries | PP Copolymer | Hifax |