NORYL PPX™ PPX630 resin
| Category: | PPE+PS+PP , Polyphenylene Ether + PS + PP |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL PPX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PVS1O6_NORYLPPXPPX630resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPX630 is a 30% glass filled alloy of PP and PPO providing design freedom for applications requiring a wide range of stiffness, toughness and temperature. Generic identification acc. ISO11469: PP+PPE-I-GF30 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 3.20 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | Internal method | ||
| Flow | 0.20 - 0.30 | % | Internal method |
| Transverse flow | 0.20 - 0.70 | % | Internal method |
| Water Absorption | |||
| Saturated, 23°C | 0.20 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.040 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 75.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 80.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 4.1 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 5500 | MPa | ISO 178 |
| Flexural Stress | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179/1eA | ||
| -30°C | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 4 | ISO 179/1eU | ||
| -30°C | 50 | kJ/m² | ISO 179/1eU |
| 23°C | 50 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact 5 | ISO 180/1A | ||
| -30°C | 10 | kJ/m² | ISO 180/1A |
| 23°C | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 6 | ISO 180/1U | ||
| -30°C | 46 | kJ/m² | ISO 180/1U |
| 23°C | 48 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7 | |||
| 0.45 MPa, unannealed, 100 mm span | 155 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 135 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 125 | °C | ISO 306/B50 |
| -- | 128 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.20 mm, in Oil) | 24 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 2.40 | IEC 60250 | |
| 60 Hz | 2.40 | IEC 60250 | |
| 1 MHz | 2.40 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 3.0E-4 | IEC 60250 | |
| 60 Hz | 3.0E-4 | IEC 60250 | |
| 1 MHz | 1.0E-3 | IEC 60250 | |
| Comparative Tracking Index | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (3.20 mm) | 650 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.0 - 75.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 245 - 290 | °C | |
| Middle Temperature | 250 - 290 | °C | |
| Front Temperature | 255 - 290 | °C | |
| Nozzle Temperature | 260 - 300 | °C | |
| Processing (Melt) Temp | 260 - 300 | °C | |
| Mold Temperature | 40.0 - 65.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 sp=62mm |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 |
| 7 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Michilene F8200 | API Polymers, Inc. | PP Copolymer | Michilene |
| Sinvicomp SFW4506 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| NEFTEKHIM PP 1500D | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| Multi-Flex® TPE A5904 LC | Multibase, A Dow Corning Company | TPE | Multi-Flex® TPE |
| Edgetek™ PC-20GF/000 NC008 | PolyOne Corporation | PC | Edgetek™ |