Panlite® MN-4800Z
| Category: | PC , Polycarbonate |
| Manufacturer: | TEIJIN LIMITED |
| Trademark: | Panlite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PUGUiu_Panlite-MN-4800Z.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Transparent Flame Retardant |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 4.00 mm | 0.50 to 0.70 | % | |
| Flow : 4.00 mm | 0.50 to 0.70 | % | |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 64.0 | MPa | ISO 527-2/50 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2270 | MPa | ISO 178 |
| Flexural Stress 2 | 98.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 122 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 7.0E-5 | cm/cm/°C | |
| Transverse | 7.0E-5 | cm/cm/°C | |
| RTI Elec (1.50 mm) | 80.0 | °C | UL 746 |
| RTI Imp (1.50 mm) | 80.0 | °C | UL 746 |
| RTI Str (1.50 mm) | 80.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50 mm | 850 | °C | |
| 2.00 mm | 850 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (3000 µm) | 88.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA III PPB200 | ROMPETROL PETROCHEMICALS S.R.L. | PP Homopolymer | MIDILENA III |
| ENFLEX S3040A | ENPLAST Americas, a Ravago Group Company | TPE | ENFLEX |
| Hylon® N1200TL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| LUVOCOM® 1-0866/BK | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| SABIC® SUPEER™ 8115 | Saudi Basic Industries Corporation (SABIC) | mLLDPE | SABIC® SUPEER™ |