Alathon® M5265
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Alathon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PUE4E0_Alathon-M5265.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Alathon M5265 is a narrow molecular weight distribution octene-copolymer used in the manufacture of open-head pails and covers. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.951 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.59 to 0.63 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.5 | g/10 min | ASTM D1238 |
| Spiral Flow | 19.6 | cm | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | ASTM D638 | ||
| -- | 764 | MPa | |
| 1% Secant | 681 | MPa | |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 26.4 | MPa | |
| Break | > 27.6 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 12 | % | |
| Break | > 2200 | % | |
| Flexural Modulus 4 | ASTM D790 | ||
| -- | 1300 | MPa | |
| 1% Secant | 1130 | MPa | |
| 2% Secant | 944 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 64 | J/m | ASTM D256 |
| Unnotched Izod Impact (-18°C) | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 69.4 | °C | ASTM D648 |
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 127 | °C | ASTM D1525 |
| Peak Melting Temperature | 132 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 118 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 232 | °C | |
| Middle Temperature | 243 | °C | |
| Front Temperature | 246 | °C | |
| Nozzle Temperature | 246 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| 3 . | Type IV, 50 mm/min |
| 4 . | 13 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4685 TFE 15 SI 2 | RTP Company | SPS | RTP |
| Milastomer™ M3800BS | Mitsui Chemicals America, Inc. | TPV | Milastomer™ |
| CP PRYME® Nylon 66 NN213HSL | Chase Plastics Services Inc. | Nylon 66 | CP PRYME® Nylon 66 |
| Elastron® V V201.A90.N | Elastron USA, Inc. | TPV | Elastron® V |
| LTP ZC-1180 | Chengdu Letian Plastics Co., Ltd | PPS, Linear | LTP |