EMERGE™ PC 4701-15
| Category: | PC , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PUD8kG_EMERGE-PC-4701-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EMERGE™ PC 4701-15 Advanced resin is formulated with 10% glass fiber and proprietary flame retardant package. It provides superb ignition resistance, rigidity, dimension stability and heat resistance. EMERGE PC 4701-15 is designed for power tools, electrical appliances and electronics parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.20 mm, Injection Molded) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.20 mm, Injection Molded) | 3650 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 3.20 mm, Injection Molded | 65.5 | MPa | |
| Break, 3.20 mm, Injection Molded | 62.7 | MPa | |
| Tensile Elongation (Break, 3.20 mm, Injection Molded) | 4.0 | % | ASTM D638 |
| Flexural Modulus (3.20 mm, Injection Molded) | 3790 | MPa | ASTM D790 |
| Flexural Strength (3.20 mm, Injection Molded) | 109 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 3.20 mm, Injection Molded) | 40 | J/m | ASTM D256 |
| Tensile Impact Strength 1(23°C, 3.20 mm, Injection Molded) | 147 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Annealed | 149 | °C | |
| 1.8 MPa, Unannealed | 141 | °C | |
| 1.8 MPa, Annealed | 135 | °C | |
| Vicat Softening Temperature | 160 | °C | ASTM D1525 2 |
| Ball Indentation Temperature | > 125 | °C | IEC 60335-1 |
| CLTE - Flow (-40 to 82°C) | 3.8E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 3 | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | 5VA | ||
| Oxygen Index 4 | 38 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 288 to 316 | °C | |
| Mold Temperature | 82.2 to 116 | °C |
| Note Message | |
|---|---|
| 1 . | Type S |
| 2 . | Rate A (50°C/h), Loading 2 (50 N) |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 4 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XYRON™ AT610 | Asahi Kasei Chemicals Corporation | Nylon+PPE | XYRON™ |
| Geon™ Fiberloc™ 80520 | PolyOne Corporation | PVC, Rigid | Geon™ Fiberloc™ |
| LNP™ STAT-KON™ DE0029 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |
| Deprene 151-80 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PP+EPDM | Deprene |
| Eco-Solutions GP1025 | Minima Technology Co., Ltd. | PLA | Eco-Solutions |