SAXALAC™ 420HI
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SAX Polymers |
| Trademark: | SAXALAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PTyKGq_SAXALAC-420HI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Saxalac 420HI is a flame retardant, very high flow ABS injection molding grade, characterized by good processability and high stiffness. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 220°C/10.0 kg | 50.0 | cm³/10min | |
| 220°C/5.0 kg | 6.00 | cm³/10min | |
| Molding Shrinkage | 0.40 to 0.70 | % | |
| Moisture Content 1 | < 0.20 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2300 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 40.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 15 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 42 | kJ/m² | |
| 23°C | 65 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180 | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 40 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 2(1.8 MPa, Unannealed, 60.0 mm Span) | 82.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 93.0 | °C | ISO 306/B50 |
| Ball Pressure Test (80°C, 2.00 mm) | Pass | IEC 60335-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (2.00 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index | 750 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | B130 |
| 2 . | 80*10*4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bayblend® M303 FR | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| Caltex PP H430 | GS Caltex | PP Homopolymer | Caltex PP |
| ANYPOL SE-300LL | SH Energy & Chemical | PS (EPS) | ANYPOL |
| Latiohm 62-09 PD01 G/20-V2HF | LATI S.p.A. | Nylon 6 | Latiohm |
| ESTOPLAST EP 2030NN01 | Ester Industries Ltd. | PBT | ESTOPLAST EP |