Elastollan® 890AN
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | BASF Corp. Thermoplastic Polyurethanes |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PTgxxy_Elastollan-890AN.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Elastollan® 890AN is specifically formulated for transparent film applications. It exhibits excellent abrasion resistance, toughness, transparency, and oil/fuel resistance. It has excellent damping characteristics and outstanding resistance to tear propagation. Elastollan®890AN conforms to the FDA food contact regulations as described in book 21, section 177.2600 and 177.1680 for both wet and dry food contact applications respectively. Elastollan® 890AN is supplied uncolored in pellet form. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/8.7 kg) | 15 to 30 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 92 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 29.0 | MPa | ASTM D412 |
| Flexural Modulus (Injection Molded) | 66.9 | MPa | ASTM D790 |
| Taber Abrasion Resistance | 45.0 | mg | ASTM D1044 |
| Abrasion - DIN | 25 | mm³ | DIN 53516 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Softening Point - DMA | 81 | °C | Internal Method |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 13.8 | MPa | |
| 300% Strain | 31.0 | MPa | |
| Tensile Strength | 39.3 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 480 | % | ASTM D412 |
| Tear Strength 1 | 144 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 23°C, 22 hr | 20 | % | |
| 70°C, 22 hr | 45 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -14.0 | °C | Internal Method |
| Vicat Softening Temperature | 120 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Rear Temperature | 190 to 220 | °C | |
| Middle Temperature | 190 to 220 | °C | |
| Front Temperature | 190 to 220 | °C | |
| Nozzle Temperature | 210 to 225 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Cylinder Zone 1 Temp. | 170 to 210 | °C | |
| Cylinder Zone 3 Temp. | 170 to 210 | °C | |
| Cylinder Zone 5 Temp. | 170 to 210 | °C | |
| Adapter Temperature | 200 to 220 | °C | |
| Die Temperature | 195 to 215 | °C |
| Note Message | |
|---|---|
| 1 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XANTAR® G4F 25 R | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Golden Compound PP S²PC 3545 BO 20LH41 | Golden Compound GmbH | PP, Unspecified | Golden Compound |
| Grilamid® L 20 LF grey | EMS-GRIVORY | Nylon 12 | Grilamid® |
| LNP™ COLORCOMP™ WX96084 compound | SABIC Innovative Plastics Europe | PBT | LNP™ COLORCOMP™ |
| Karina IVORY PVC COMPOUND -E 105853-35/ 1-B-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |