Order Products : sales@su-jiao.com
AGILITY™ 6047
| Category: | HDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | AGILITY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PTYqFX_AGILITY-6047.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AGILITY 6047 is a Linear Medium Density Polyethylene, 1-Octene Copolymer from Dow. This resin offers good mechanical properties and toughness, with the required features for the production of diapers and products for feminine hygiene. This product is easy to process and has good web stability at high speed machines. Main Characteristics:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.947 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Film Puncture Resistance (20 µm) | 0.485 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| TD : 20 µm | 512 | MPa | ASTM D882 |
| 1% secant, TD : 20 µm | 428 | MPa | ASTM D882 |
| 2% secant, TD : 20 µm | 327 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 20 µm | 15.1 | MPa | ASTM D882 |
| TD : Yield, 20 µm | 15.1 | MPa | ASTM D882 |
| MD : Break, 20 µm | 12.0 | MPa | ASTM D882 |
| TD : Break, 20 µm | 10.3 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield, 20 µm | 9.7 | % | ASTM D882 |
| TD : Yield, 20 µm | 6.3 | % | ASTM D882 |
| MD : Break, 20 µm | 260 | % | ASTM D882 |
| TD : Break, 20 µm | 85 | % | ASTM D882 |
| Dart Drop Impact (20 µm) | 52 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 20 µm | 43 | g | ASTM D1922 |
| TD : 20 µm | 84 | g | ASTM D1922 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 235 | °C |
| Extrusion instructions |
|---|
| Recommended Processing Conditions for extrusion Cast for 20 um film: Die gap: 0,3 mm Line Speed: 19,7 m/min Melt Pressure: 81 bar Melt Temperature: 235°C Output: 7 kg/h Speed: 75 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP5113 B1 | Spartech Polycom | PP, Unspecified | Spartech |
| GERMAMID 6.6 GF 30 MO | Kunststoff-Kontor-Hamburg GmbH | Nylon 66 | GERMAMID |
| Infino LB-1010W | SAMSUNG SDI CO., LTD. | PC | Infino |
| LNP™ THERMOCOMP™ DX06094 compound | SABIC Innovative Plastics Europe | PC | LNP™ THERMOCOMP™ |
| POLYFORT® FPP 20 T | A. Schulman Europe | PP Homopolymer | POLYFORT® |