| KOCETAL® CN301C3 is carbon nanotube (CNT) reinforced grade for electrical conductivity |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.9 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.22 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 80 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (23°C) | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 15 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2300 | MPa | ISO 178 |
| Flexural Stress (23°C) | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.5 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 96.0 | °C | ISO 75-2/A |
| Melting Temperature | 166 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+2 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.8 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 - 90 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 180 | °C | |
| Middle Temperature | 190 | °C | |
| Front Temperature | 190 | °C | |
| Nozzle Temperature | 200 | °C | |
| Processing (Melt) Temp | < 220 | °C | |
| Mold Temperature | 60 - 80 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP852 | Southern Polymer, Inc. | HDPE, HMW | PRIMALENE |
| PROTEQ™ C17T4 | Marplex Australia Pty. Ltd. | PP Copolymer | PROTEQ™ |
| Ultramid® A3Z | BASF Corporation | Nylon 66 | Ultramid® |
| MAJORIS EFR201 | AD majoris | PP, Unspecified | MAJORIS |
| Sylvin 8299-75 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |