Fiberfil® J-60/30/E5
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Fiberfil® Engineered Plastics Inc. |
| Trademark: | Fiberfil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PSlHKZ_Fiberfil-J-60-30-E5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fiberfil®J-60/30/E5 is a polypropylene homopolymer (PP Homopoly) material, and the filler is 30% glass fiber reinforced material. This product is available in North America,. Fiberfil®The main features of J-60/30/E5 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18 mm | 0.30 | % | ASTM D955 |
| 6.35 mm | 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.030 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 5860 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 82.7 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 3.0 | % | ASTM D638 |
| Flexural Modulus - Tangent (23°C) | 4830 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 107 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 157 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 152 | °C | ASTM D648 |
| Additional Information |
|---|
| Rockwell Hardness, ASTM D785, R-Scale: 100 to 110 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Geon™ HC 2190G | PolyOne Corporation | PVC, Flexible | Geon™ HC |
| LNP™ THERMOCOMP™ RX06420 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| LNP™ THERMOCOMP™ AF008 compound | SABIC Innovative Plastics | ABS | LNP™ THERMOCOMP™ |
| Polyfast SA003 | Ravago Group | ASA | Polyfast |
| Elastoflex® W 5666/103 | BASF Polyurethanes GmbH | PUR-MDI | Elastoflex® |