Braskem PP CP 195
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Braskem |
| Trademark: | Braskem PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PSfx1G_Braskem-PP-CP-195.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: CP 195 is a very high melt flow rate heterophasic copolymer developed for high speed injection moulding machines and high productivity thin-walled injection moulded parts. The product features high impact strength even at sub-zero temperatures and it is suitable for food contact applications due to its excellent organoleptic properties. Applications: Household; Low temperature packing; Frozen desserts packing; Packages with excellent organoleptic properties. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.895 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 60 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale, Injection Molded | 39 | ASTM D785 | |
| R-Scale | 39 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, Injection Molded) | 19.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Yield, Injection Molded) | 5.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus - 1% Secant | |||
| Injection Molded | 850 | MPa | ASTM D790 |
| Injection Molded | 1000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -20°C, Injection Molded | 60 | J/m | ASTM D256 |
| 23°C, Injection Molded | 160 | J/m | ASTM D256 |
| -20°C, Injection Molded | 5.5 | kJ/m² | ISO 180 |
| 23°C, Injection Molded | 8.2 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, Injection Molded | 93.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 93.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, Injection Molded | 53.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 53.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 137 | °C | ISO 306/A, ASTM D1525 1 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® PSH 6132 | Marco Polo International, Inc. | PS (HIPS) | MARPOL® PSH |
| Algoflon® S 121 | Solvay Specialty Polymers | PTFE | Algoflon® |
| Electrafil® ABS SS10 FR BK | Techmer Engineered Solutions | ABS | Electrafil® |
| Karina GREEN COLOR CONCENTRATE 40/135-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| REPOL® SS80N | Reliance Industries Limited | PP Homopolymer | REPOL® |