Niretan B AE/V0
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Soredi S.p.a. |
| Trademark: | Niretan B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PSINbH_Niretan-B-AE-V0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6 flame retardant as per UL 94 V0 at 1.6 mm rating |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.16 | -- | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 9.0 | 10 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.5 | 3.4 | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | 102 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | |||
| Yield | 80.0 | 40.0 | MPa | ASTM D638 |
| Fracture | 60.0 | 30.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 60 | 200 | % | ASTM D638 |
| Flexural Modulus 3 | 2800 | 800 | MPa | ASTM D790 |
| Flexural Strength 4(Break) | 120 | 60.0 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| 0°C, 3.20 mm | 45 | 500 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 50 | 600 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 70.0 | -- | °C | ASTM D648 |
| Peak Crystallization Temperature (DSC) | 215 | 220 | °C | ASTM D3418 |
| CLTE - Flow | 7.5E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+11 | ohms·cm | IEC 60093 |
| Dielectric Strength (1.00 mm) | 60 | 40 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.80 | -- | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.030 | -- | IEC 60250 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | V-0 | -- | UL 94 | |
| 3.20 mm | V-0 | -- | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 960 | -- | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 干燥 Tensile Elongation at Break, ASTM D638, 5 mm/min: >60% |
| 调节后的 Tensile Elongation at Break, ASTM D638, 5 mm/min: >200% |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKNIFLEX® VA10300 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PCTFE | TEKNIFLEX® |
| ELASTOSIL® E 60 N grey | Wacker Chemie AG | Silicone | ELASTOSIL® E |
| Epic Urethane S7344 | Epic Resins | PUR, Unspecified | Epic Urethane |
| Hanwha Total PP RP100N120 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Braskem PE LDF0223 | Braskem IDESA | LDPE | Braskem PE |