EcoPaXX® Q210E-H
| Category: | Nylon 410 , Polyamide 410 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | EcoPaXX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PRhnEz_EcoPaXXQ210EH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EcoPaXX®Q210E-H is a Polyamide 410 (Nylon 410) material,. This product is available in North America, Europe or Asia Pacific,. EcoPaXX®The main features of the Q210E-H are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.09 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 5.8 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.9 | -- | % | ISO 62 |
| Viscosity Number | 210 | -- | cm³/g | ISO 307 |
| Biomass Content- Bio C/Total C 1 | 70 | -- | % | ASTM D6866 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3000 | 1600 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Yield | 80.0 | 55.0 | MPa | ISO 527-2 |
| Fracture | 55.0 | 40.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | |||
| Yield | 4.4 | 15 | % | ISO 527-2 |
| Fracture | 30 | > 50 | % | ISO 527-2 |
| Flexural Modulus | 2850 | 1400 | MPa | ISO 178 |
| Flexural Stress | 115 | 55.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | 13 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 175 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 77.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 2 | 250 | -- | °C | ISO 11357-3 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 - 8.0 | hr | |
| Rear Temperature | 250 - 270 | °C | |
| Middle Temperature | 260 - 280 | °C | |
| Front Temperature | 270 - 290 | °C | |
| Nozzle Temperature | 270 - 300 | °C | |
| Processing (Melt) Temp | 270 - 300 | °C | |
| Mold Temperature | 60 - 100 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 - 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMIKASUPER® LCP E6710 | Sumitomo Chemical Co., Ltd. | LCP | SUMIKASUPER® LCP |
| XENOY™ HX5600HP resin | SABIC Innovative Plastics | PC+PBT | XENOY™ |
| ACCUTECH™ HP0334W40L1 | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| DOWLEX™ 3010 | The Dow Chemical Company | LLDPE | DOWLEX™ |
| Keliren® CM402 | Hangzhou Keli Chemical Co., Ltd. | CPE | Keliren® |