LNP™ STAT-KON™ Noryl_NC2525 compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PQGqVd_LNP-STAT-KON-Noryl-NC2525-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP STAT-KON NORYL_NC2525 compound is a 25% CFR PPE+PS. Highly conductive. High heat. May be added to similar material/regrind to add some conductivity to the blend. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.40 to 0.60 | % | |
| Across Flow : 3.20 mm | 0.45 to 0.65 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 20700 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 107 | MPa | |
| Break | 107 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 2.5 | % | |
| Break | 2.5 | % | |
| Flexural Modulus 4(50.0 mm Span) | 15900 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 50.0 mm Span) | 148 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 180 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 9.04 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 178 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 171 | °C | |
| Vicat Softening Temperature | 179 | °C | ASTM D1525 6 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 1.8E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 1.1E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 | ohms | ASTM D257 |
| Volume Resistivity | 0.30 | ohms·cm | ASTM D257 |
| Static Decay 7 | 10 | msec | FTMS 101B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 121 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 293 to 321 | °C | |
| Middle Temperature | 299 to 327 | °C | |
| Front Temperature | 299 to 335 | °C | |
| Nozzle Temperature | 304 to 335 | °C | |
| Processing (Melt) Temp | 304 to 335 | °C | |
| Mold Temperature | 93.3 to 132 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 100 | rpm | |
| Vent Depth | 0.038 to 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | Rate B (120°C/h), Loading 2 (50 N) |
| 7 . | 5000V to <50V |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starex VG-4910 | SAMSUNG SDI CO., LTD. | ABS | Starex |
| SWANCOR Epoxy 901-35 | SWANCOR IND. CO., LTD. | Epoxy | SWANCOR Epoxy |
| BJB Silicone TC-5060 A/B | BJB Enterprises, Inc. | Silicone | BJB Silicone |
| Catalyst PS/2LRO | Solvay Specialty Polymers | Polyolefin, Unspecified | Catalyst |
| Fainplast PVC CRK 84 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |