LNP™ LUBRICOMP™ DP001E compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PQASx3_LNP-LUBRICOMP-DP001E-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* DP001E is a Polycarbonate base resin containing 5% PTFE/Silicone. Added features of this material include: Easy Molding, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound DL-4510 EM Product reorder name: DP001E |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.30 to 0.50 | % | |
| Across Flow : 24 hr | 0.50 to 0.70 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.12 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.17 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2240 | MPa | ASTM D638 |
| -- | 2130 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 54.0 | MPa | ASTM D638 |
| Yield | 54.0 | MPa | ISO 527-2/5 |
| Break 3 | 45.0 | MPa | ASTM D638 |
| Break | 41.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 6.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/5 |
| Break 5 | 38 | % | ASTM D638 |
| Break | 48 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2230 | MPa | ASTM D790 |
| -- 7 | 2030 | MPa | ISO 178 |
| Flexural Stress | 72.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.21 | ||
| vs. Itself - Static | 0.11 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 0.100 to 0.200 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 154 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 600 | J/m | ASTM D256 |
| 23°C 8 | 36 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1500 | J/m | ASTM D4812 |
| 23°C 9 | 180 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 35.2 | J | ASTM D3763 |
| -- | 44.7 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 141 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 140 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 127 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 126 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 6.9E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 7.1E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 304 to 316 | °C | |
| Front Temperature | 310 to 321 | °C | |
| Processing (Melt) Temp | 299 to 316 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC4SCE (Series: SCR) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Borealis PE BB2581 | Borealis AG | HDPE | Borealis PE |
| Kepital® TE-24 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| LUVOCOM® 1106-7940/GY/EM | Lehmann & Voss & Co. | PEI | LUVOCOM® |
| Plaslube® AC-81/TF/20/Natl | Techmer Engineered Solutions | Acetal (POM) Homopolymer | Plaslube® |