Grivory® G 16
| Category: | Nylon 6I/6T , Polyamide 6I/6T Copolymer |
| Manufacturer: | EMS-GRIVORY |
| Trademark: | Grivory® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PPoUog_Grivory-G-16.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Grivory® G 16 is a Polyamide 6I/6T Copolymer (Nylon 6I/6T) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for extrusion or injection molding. Important attributes of Grivory® G 16 are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.18 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 100 | -- | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 7.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3000 | 3000 | MPa | ISO 527-2 |
| Films | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress | ISO 527-3 | |||
| MD : Yield | 85.0 | -- | MPa | |
| TD : Yield | 85.0 | -- | MPa | |
| MD : Break | 80.0 | -- | MPa | |
| Tensile Elongation | ISO 527-3 | |||
| MD : Yield | 5.0 | -- | % | |
| TD : Yield | 5.0 | -- | % | |
| MD : Break | 200 | -- | % | |
| TD : Break | 200 | -- | % | |
| Elmendorf Tear Strength | ISO 6383-2 | |||
| MD | 10 | -- | N | |
| TD | 10 | -- | N | |
| Trouser Tear Resistance | ISO 6383-1 | |||
| MD | 5.00 | -- | N/mm | |
| TD | 5.00 | -- | N/mm | |
| Water Vapor Transmission Rate (23°C, 85% RH) | 7.0 | -- | g/m²/24 hr | DIS 15106-1/-2 |
| Oxygen Transmission Rate | DIS 15105-1/-2 | |||
| 23°C 1 | 30 | -- | cm³/m²/bar/24 hr | |
| 23°C 2 | 10 | -- | cm³/m²/bar/24 hr | |
| Carbon Dioxide Transmission Rate | DIS 15105-1/-2 | |||
| 23°C 3 | 40.0 | -- | cm³/m²/bar/24 hr | |
| 23°C 4 | 90.0 | -- | cm³/m²/bar/24 hr |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Type | PA 6I/6T, FT, 09-030 | -- | ISO 1874 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 8.0 | 2.0 | kJ/m² | |
| 23°C | 8.0 | 8.0 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Glass Transition Temperature 5 | 125 | -- | °C | ISO 11357-2 |
| Optical | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Gloss (60°) | 160 | -- | ISO 2813 |
| Note Message | |
|---|---|
| 1 . | 0% RH |
| 2 . | 85% RH |
| 3 . | 85% RH |
| 4 . | 0% RH |
| 5 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Tech™ X3 ST6000-5006 FR BLACK | PolyOne Corporation | Nylon 6 | Stat-Tech™ |
| NatureFlex™ 140NP | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| COSMOPLENE® FL7540 | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP Random Copolymer | COSMOPLENE® |
| Lucofin® 1413 | Lucobit AG | Polyolefin, Unspecified | Lucofin® |
| ALCUDIA® HDPE 51100 | REPSOL | HDPE | ALCUDIA® HDPE |