Stat-Tech™ NN-20CF/000 Black HS

Category:	Nylon 66 , Polyamide 66
Manufacturer:	PolyOne Corporation
Trademark:	Stat-Tech™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	PPO0xN_Stat-Tech-NN-20CF-000-Black-HS.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compounds combine the performance of select engineering resins with reinforcing additives such as carbon powder, carbon fiber, nickel-coated carbon fiber and stainless steel fiber for low to high levels of conductivity depending upon application requirements.

General Information
Filler / Reinforcement	Carbon Fiber, 20% Filler by Weight
Features	Good Chemical Resistance High Heat Resistance High Stiffness Semi Crystalline
Uses	Aerospace Applications Automotive Electronics Business Equipment Computer Components Connectors Consumer Applications Electrical Housing Electrical/Electronic Applications Housings Sporting Goods
RoHS Compliance	RoHS Compliant
Forms	Pellets
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.22	g/cm³	ASTM D792
Molding Shrinkage			ASTM D955
Flow	0.050 to 0.20	%
Across Flow	1.7 to 1.9	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus ¹	12800	MPa	ASTM D638
Tensile Strength (Break)	172	MPa	ASTM D638
Tensile Elongation ²(Break)	2.2	%	ASTM D638
Flexural Modulus	11900	MPa	ASTM D790
Flexural Strength	231	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C, 3.18 mm, Injection Molded)	48	J/m	ASTM D256A

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, Unannealed, 6.35 mm	261	°C
1.8 MPa, Unannealed, 6.35 mm	250	°C

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+2 to 1.0E+4	ohms	ASTM D257
Volume Resistivity	1.0E+2 to 1.0E+4	ohms·cm	ASTM D257
Static Decay - (Mil-B-81705C), 12% RH, 5000 kV to 50 kV	0.003	sec

Injection	Nominal Value	Unit
Processing (Melt) Temp	288 to 304	°C

Note Message
1 .	Type I, 5.1 mm/min
2 .	Type I, 5.1 mm/min

Resin Grade	Manufacturer	Category	Trademark
Teldene® H03BPMP	National Petrochemical Industries Company (NATPET)	PP Homopolymer	Teldene®
TPSiV™ 4200-70A	Multibase, A Dow Corning Company	TPSiV	TPSiV™
TOTAL Polypropylene Lumicene® MR 110MC2	TOTAL Refining & Chemicals	PP Random Copolymer	TOTAL Polypropylene
Hylex® P1310G10FRMA	Ravago Manufacturing Americas, LLC	PC	Hylex®
Mediprene® 502534M	ELASTO	TPE	Mediprene®