LNP™ THERMOCOMP™ LCF62E compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PPH4iv_LNP-THERMOCOMP-LCF62E-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP LCF62E is a compound based on Polyetheretherketone resin containing 10% Carbon, 30% Glass Fiber fillers. Added features of this material includes: Easy Molding, Electrically Conductive. Also known as: LNP* THERMOCOMP* Compound LCF-1008 EM Product reorder name: LCF62E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.57 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.090 to 2.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.026 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.026 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 63000 | MPa | ASTM D638 |
| -- | 41100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 204 | MPa | ASTM D638 |
| Break | 196 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 0.87 | % | ASTM D638 |
| Break | 0.74 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 17300 | MPa | ASTM D790 |
| -- 5 | 36500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 391 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 297 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 80 | J/m | ASTM D256 |
| 23°C 7 | 8.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 710 | J/m | ASTM D4812 |
| 23°C 8 | 48 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 17.4 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 290 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 290 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 290 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 290 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 370 to 380 | °C | |
| Middle Temperature | 380 to 400 | °C | |
| Front Temperature | 380 to 400 | °C | |
| Mold Temperature | 175 to 190 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Tech™ AT-CB2/000 CR | PolyOne Corporation | Acetal (POM) Copolymer | Stat-Tech™ |
| Adell Polyamide AT-14 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| Ferro PP LPP20BN47HB BLACK | Ferro Corporation | PP Copolymer | Ferro PP |
| Gallonprene® GP520-9009 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| LEXAN™ XHT3171 resin | SABIC Innovative Plastics | PC | LEXAN™ |