ISPLEN® PR 264 G1F

Category:	PP Random Copolymer , Polypropylene Random Copolymer
Manufacturer:	REPSOL
Trademark:	ISPLEN®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	POEiLg_ISPLEN-PR-264-G1F.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
ISPLEN® PR 264 G1F is a polypropylene random copolymer with medium melt flow rate propylene-ethylene random copolymer. Films prepared with ISPLEN® PR 264 G1F have both excellent optical properties and mechanical properties, and is normally used for packaging (foodstuffs, textiles, stationery, organizational office aids, flowers…). In co-extrusion or lamination it gives the film good heat-sealing characteristics. It can be easily coloured during the extrusion process using the right pigments, preferably in the form of concentrates with a higher melt flow rate than that of the base polymer. TYPICAL APPLICATIONS In applications requiring high transparency and gloss: Extrusion and/or Co-extrusion Non-oriented film, Cast-film Tubular quench Recommended melt temperature range from 190 - 250°C. Processing conditions should be optimised for each production line.

Message

ISPLEN® PR 264 G1F is a polypropylene random copolymer with medium melt flow rate propylene-ethylene random copolymer.
Films prepared with ISPLEN® PR 264 G1F have both excellent optical properties and mechanical properties, and is normally used for packaging (foodstuffs, textiles, stationery, organizational office aids, flowers…). In co-extrusion or lamination it gives the film good heat-sealing characteristics. It can be easily coloured during the extrusion process using the right pigments, preferably in the form of concentrates with a higher melt flow rate than that of the base polymer.

TYPICAL APPLICATIONS
In applications requiring high transparency and gloss:

Extrusion and/or Co-extrusion

Non-oriented film, Cast-film

Tubular quench

Recommended melt temperature range from 190 - 250°C. Processing conditions should be optimised for each production line.

General Information
Features	Food Contact Acceptable Good Colorability Good Heat Seal Medium Flow Opticals
Uses	Cast Film Film Food Packaging Laminates Non-oriented Film Packaging
Agency Ratings	EU Food Contact, Unspecified Rating
Processing Method	Cast Film Coextrusion Extrusion

Physical	Nominal Value	Unit	Test Method
Density	0.905	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	9.0	g/10 min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Flexural Modulus	950	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	6.0	kJ/m²	ISO 179

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (0.45 MPa, Unannealed)	70.0	°C	ISO 75-2/B
Vicat Softening Temperature	138	°C	ISO 306/A

Extrusion	Nominal Value	Unit
Melt Temperature	190 to 250	°C

Resin Grade	Manufacturer	Category	Trademark
TEKNILID HS165	Tekni-Films, a div of Tekni-Plex	Film, Al Foil/Polyester	TEKNILID
Vistalon™ 2504	ExxonMobil Chemical	EPDM	Vistalon™
Huafon JF-A-WV1008B	Huafon Group Co., Ltd.	PUR, Unspecified	Huafon
Hylex® P1010G7FRMA	Ravago Manufacturing Americas, LLC	PC	Hylex®
Jampilen RP270G	Jam Polypropylene Company	PP Random Copolymer	Jampilen