Quadrant EPP Nylatron® GSM Blue
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Quadrant EPP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PNkNBo_Quadrant-EPP-Nylatron-GSM-Blue.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylatron GSM Blue nylon is the first cast nylon to combine both molybdenum disulfide and oil for the load capability of Nylatron GSM nylon, plus improved frictional characteristics. It excels in higher pressures, and at low speeds- up to 40 fpm. It offer 20% lower coefficient of friction, 50% greater limiting PV, and a lower "k" factor than Nylatron GSM, and the lowest "slip-stick" of any nylon product. It is ideal for slide pads, thrust washers and trunion bearings. Nylatron GSM blue should be considered for any oil-filled nylon application. It is dark blue in color. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.30 | % | |
| Saturation | 6.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 80 | ||
| R-Scale | 117 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3450 | MPa | ASTM D638 |
| Tensile Strength (Ultimate) | 68.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 30 | % | ASTM D638 |
| Flexural Modulus | 3450 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 103 | MPa | ASTM D790 |
| Compressive Modulus | 2930 | MPa | ASTM D695 |
| Compressive Strength (10% Strain) | 89.6 | MPa | ASTM D695 |
| Coefficient of Friction (vs. Steel - Static) | 0.18 | Internal Method | |
| Wear Factor | 130 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 48 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 93.3 | °C | ASTM D648 |
| Maximum Use Temperature - Long Term, Air | 93 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Limiting Pressure Velocity 1 | 0.193 | MPa·m/s | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 216 | °C | ASTM D3418 |
| CLTE - Flow 2(-40 to 149°C) | 9.9E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 3 | > 1.0E+13 | ohms | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.18 mm, Estimated Rating) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 4:1 safety factor |
| 2 . | 68°F |
| 3 . | EOS/ESD S11.11 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 TFE 20 HS | RTP Company | Nylon 66 | RTP |
| Polymist® XPP 541 | Solvay Specialty Polymers | PTFE | Polymist® |
| Clariant PC PC-1100G30TF15 | Clariant Corporation | PC | Clariant PC |
| Haysite SMC 54500 | Haysite Reinforced Plastics | Polyester, TS | Haysite SMC |
| Kepital® ET-20H | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |