WELLAMID Nylon 6000 CF 30 HWCP
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | CP-Polymer-Technik GmbH & Co. KG |
| Trademark: | WELLAMID Nylon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PNWONB_WELLAMID-Nylon-6000-CF-30-HWCP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WELLAMID Nylon 6000 CF 30 HWCP is a Polyamide 6 (Nylon 6) material filled with 30% carbon fiber. It is available in Europe. Important attributes of WELLAMID Nylon 6000 CF 30 HWCP are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.25 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 4.00 mm | 0.80 | -- | % | |
| Flow : 4.00 mm | 0.20 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.8 to 2.3 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 21000 | 16000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 200 | 140 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.5 | 3.5 | % | ISO 527-2/5 |
| Flexural Modulus | 18500 | -- | MPa | DIN 52457 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | 18 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 42 | 78 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 210 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 200 | -- | °C | ISO 306/B50 |
| Melting Temperature | 215 | -- | °C | |
| CLTE - Flow (23 to 80°C) | 2.5E-5 | -- | cm/cm/°C | DIN 53752 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | < 10 | -- | ohms | IEC 60093 |
| Volume Resistivity | < 5.0 | -- | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 70.0 to 100 | °C | |
| Injection Rate | Moderate-Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ASTALAC™ ABS X13 | Marplex Australia Pty. Ltd. | ABS | ASTALAC™ |
| Aropol™ MR 14029 | Ashland Performance Materials | Polyester, TS | Aropol™ |
| Clariant Nylon 6/6 PA-123 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Pearlthane® ECO D12T85 | Lubrizol Advanced Materials, Inc. | TPU-Polyester | Pearlthane® ECO |
| PELPRENE™ P80C | TOYOBO America, Inc. | TPEE | PELPRENE™ |