Tarnamid® T- 27 Z1
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Grupa Azoty S.A. |
| Trademark: | Tarnamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PNAQCY_Tarnamid-T--27-Z1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Impact modified. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.11 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 110 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (2.00 mm) | 0.70 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 9.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.8 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 150 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2800 | -- | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 72.0 | -- | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 40 | -- | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2200 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 75.0 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 10 | -- | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength | 10 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 55.0 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 195 | -- | °C | ISO 306/B |
| Melting Temperature | 221 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+16 | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 21 | 19 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 Hz) | 3.40 | 3.50 | IEC 60250 | |
| Dissipation Factor (1 Hz) | 0.020 | 0.10 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (3.20 mm) | HB | -- | UL 94 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Type | PA6-HI, MR, 14020 | -- | ISO 1874 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Suggested Max Moisture | < 0.10 | % | |
| Suggested Max Regrind | 50 | % | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Pressure | 80.0 to 110 | MPa | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Wire & Cable GA-1046CTLF | S&E Specialty Polymers, LLC | PVC, Semi-Rigid | S&E Wire & Cable |
| Hifax TRS 784D | LyondellBasell Industries | TPO (POE) | Hifax |
| Lucel® FW715CS | LG Chem Ltd. | Acetal (POM) Copolymer | Lucel® |
| MACOMASS PVC MM-PVC E 1570 | MACOMASS Verkaufs AG | PVC, Flexible | MACOMASS PVC |
| POLYfill PP HJ752 UV2 | Polykemi AB | PP, Unspecified | POLYfill |