Kepital® TX-11H
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepital® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PMBt2n_Kepital-TX-11H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A medium-high viscosity grade for general injection molding. It is suitable for use requiring reduced wear noise, and a good friction & wear resistance without sacrificing mechanical properties. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 5.0 | g/10 min | ASTM D1238 |
| -- | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.00mm | 2.0 | % | ASTM D955 |
| 3.00 mm | 2.0 | % | |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.22 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 80 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C | 60.0 | MPa | ASTM D638 |
| Yield, 23°C | 64.0 | MPa | ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 60 | % | ASTM D638 |
| Nominal Tensile Strain at Break (23°C) | 40 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2500 | MPa | ASTM D790 |
| 23°C | 2550 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 82.0 | MPa | ASTM D790 |
| 23°C | 86.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D1894 | ||
| With Metal-Dynamic | 0.27 | ASTM D1894 | |
| With self-dynamics | 0.22 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 7.5 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (3.20 mm) | 78 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 158 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 110 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 97.0 | °C | ISO 75-2/A |
| Peak Melting Temperature | 165 | °C | ASTM D3418 |
| CLTE - Flow (20 to 80°C) | 1.3E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257, IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Additional Information |
|---|
| Specific Wear, Resin vs. Resin: 2.5 mm³/Kg*KmSpecific Wear, Resin vs. Metal: 0.02 mm³/Kg*Km |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RESOLE RX®643 | Vyncolit N.V. | Phenolic | RESOLE |
| SLOVASTER® B1 HML GF 10 | Plastcom | PBT | SLOVASTER® |
| WELLAMID Nylon 6000/50 HWUVCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| XYLEX™ X8210 resin | SABIC Innovative Plastics Europe | PC+Polyester | XYLEX™ |
| Moplen RP210G | LyondellBasell Industries | PP Random Copolymer | Moplen |